Sikaflex® NP 150 Series 50446486 Elastomeric Joint Sealant
Sikaflex® NP 150 Series 50446486 Elastomeric Joint Sealant
Sikaflex® HY 150 is a high-performance, very low-modulus, high-movement, non-sag, fast-curing, hybrid sealant.
Sikaflex® Elastomeric Joint Sealant, NP 150 Series, 20 oz Net Content, Cartridge Container, Paste Form, White, Composition: >=20 to <50% calcium carbonate, >=5 to <10% Limestone, >=1 to <3% carbon black, >=0.3 to <3% stearic acid, >=0.3 to <1% N-(3- (Trimethoxysilyl)propyl)ethylene diamine, >=0.1 to <0.2% Dibutylbis(pentane-2,4-dionatoO,O')tin, >=0.2 to <1% 2-(2H-Benzotriazol-2-yl)-4,6- ditertpentylphenol, >=0.2 to <1% bis(2,2,6,6-tetramethyl-4- piperidyl)sebacate, 90 min Dry Time, 1 week Curing Time, 154 linear ft Coverage Area, Density: 12.2 lb/gal, Heavier Than Air Vapor Density, 140 to 180 psi Tensile Strength, Applicable Materials: Aluminum, Concrete, Fiber, Masonry, Metal, Stone, Vinyl, Wood, 15 months Shelf Life, -40 to 180 deg F, 800 to 1000% Elongation
| Additional Information | : | 800 to 1000% Elongation |
| Applicable Materials | : | Aluminum, Concrete, Fiber, Masonry, Metal, Stone, Vinyl, Wood |
| Color | : | White |
| Composition | : | >=20 to <50% calcium carbonate, >=5 to <10% Limestone, >=1 to <3% carbon black, >=0.3 to <3% stearic acid, >=0.3 to <1% N-(3- (Trimethoxysilyl)propyl)ethylene diamine, >=0.1 to <0.2% Dibutylbis(pentane-2,4-dionatoO,O')tin, >=0.2 to <1% 2-(2H-Benzotriazol-2-yl)-4,6- ditertpentylphenol, >=0.2 to <1% bis(2,2,6,6-tetramethyl-4- piperidyl)sebacate |
| Container Type | : | Cartridge |
| Coverage Area | : | 154 linear ft |
| Curing Time | : | 1 week |
| Density | : | 12.2 lb/gal |
| Dry Time | : | 90 min |
| Form | : | Paste |
| Net Content | : | 20 oz |
| Series | : | NP 150 Series |
| Shelf Life | : | 15 months |
| Temperature Rating | : | -40 to 180 deg F |
| Tensile Strength | : | 140 to 180 psi |
| Vapor Density | : | Heavier Than Air |
- Superior adhesion results in a long-lasting bond, helping to reduce callbacks
- Low modulus to accommodate for joint movement (100% extension in EIFS joints with little stress on bond line)
- Can be painted with elastomeric coatings soon after installation. Easy to gun and tool, speeding up application
- Wide temperature application range
- Weather resistant for long-lasting weathertight seals
- Fast curing helps to speed up job site production
- Non-staining formula for use on stone and other sensitive substrates
- Meets all state and federal VOC regulations
- Can adhere to green concrete in as little as 72 hours after pour
- Adheres to low-energy surfaces including polyethylene, polypropylene, and polyolefins